C17510 CuNi2Be Beryllium Copper Plate 140mmX45mmX2000mm For Industry

Place of Origin China
Certification ISO ROHS
Model Number C17510 CuNi2Be
Minimum Order Quantity 30kg
Price USD 30~50/KG
Packaging Details Pack in coil+waterproofing winding film+Drier+Wooden Case
Delivery Time 10~15 Working days
Payment Terms L/C, T/T
Supply Ability 50T/Month

Contact me for free samples and coupons.

Whatsapp:0086 18588475571

Wechat: 0086 18588475571

Skype: sales10@aixton.com

If you have any concern, we provide 24-hour online help.

Product Details
Name C17510 CuNi2Be Beryllium Copper Plate Size 140mm*45mm*2000mm
ASTM ASTM B534 Temper TF00
Surface Bright Heat Treatment 3 Hr 315C-330C
Typical Application Plastic Moulds Application Industry
High Light

CuNi2Be Beryllium Copper Plate


Industry Beryllium Copper Sheet


C17510 Beryllium Copper Plate

Leave a Message
Product Description

C17510 CuNi2Be Beryllium Copper Plate 140mm*45mm*2000mm Used In Industry Application

Product Normal Description:

Product Name: Beryllum copper plate

Grade: C17510, CuNi2Be

Standard: ASTM B534

Product Size: 140mm x 45mm x 2000mml

State: TF00

Typical Application: Industry

Product Brand: CUBERYLLIUM®


Chemical Composition:

CUBERYLLIUM® Brand UNS-Number Beryllium Nickel Fe Si Copper
Cuberyllium-C751 C17510 0.20-0.60 1.4~2.2 <0.1 <0.2 Balance

Note: Copper plus additions equal 99.5% Minimum.


Beryllium Copper Alloys:

Beryllium copper (C17200 & C17300) is an age-hardening alloy which attains the highest strength of any copper-base alloy. It may be age-hardened after forming into springs, intricate forms or complex shapes. It is esteemed for spring properties, erosion obstruction, soundness, conductivity, and low creep.
Tempered beryllium copper is C17200 and C17300 that has been age solidified and cold drawn. No further heat treatment is essential past a potential light pressure alleviation. It is adequately flexible to twist without anyone else measurement and can be framed into springs and most shapes. The tempered wire is most valuable where the properties of beryllium copper are wanted, yet the age solidifying of completed parts isn’t useful.
C17510 and C17500 beryllium copper alloys are age-hardenable and give great electrical conductivity, physical properties, and perseverance. They are utilized in springs and wire where electrical conduction or maintenance of properties at raised temperatures is significant.
High-quality beryllium copper combinations contain as much as 2.7% beryllium (cast), or 1.6-2% beryllium with about 0.3% cobalt (created).
High conductivity beryllium copper combinations contain as much as 0.7% beryllium with some nickel and cobalt. The thermal conductivity of these amalgams is more prominent than aluminum and somewhat not exactly unadulterated copper and are regularly utilized as electrical contacts.


Typical Physical Properties of C17510 CuNi2Be Beryllium Copper Alloy:

Coefficient of Thermal Expansion 9.8 . 10-6 per oF (68-392 F) 17.6 . 10 6 per C (20-200 C)
Density 0.317 lb/in3 @ 68 F 8.77 gm/cm3 @ 20 C
Electrical Conductivity 48 %IACS @ 68 F 0.281 MegaSiemens/cm @ 20 C
Electrical Conductivity 45 %IACS @ 68 F 0.263 MegaSiemens/cm @ 20 C
Electrical Resistivity 22.8 ohms-cmil/ft @ 68 F 3.79 microhm-cm @ 20 C
Melting Point Liquid US 1955 F 1068 C
Melting Point Solid US 1885 F 1029 C
Modulas of Elasticity in Tension 19200 ksi 132400 MPa
Modulas of Rigidity 7500 ksi 51710 MPa
Specific Gravity 8.77 8.77
Specific Heat Capacity 0.1 Btu/lb/F @ 68 F 419.0 J/kg . K at 293 K
Thermal Conductivity 120.0 Btu . ft/(hr . ft2 . F) @ 68 F 207.7 W/m . K at 20 C


Typical Applications of C17510 CuNi2Be Beryllium Copper Alloy:

• Bearings and bushes
• Plastic moulds
• Corrosion resistant components
• Current carrying springs
• Welding electrodes
• Electrical and electronic connectors


Product Photo:

C17510 CuNi2Be Beryllium Copper Plate 140mmX45mmX2000mm For Industry 0



Soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding are all recommended

Corrosion Resistance

Alloy 751’s corrosion resistance is similar to pure copper. It resists corrosion in sea water, most organic solutions, non- oxidizing acids, and dilute alkalis. Alloy 751 is not subject to hydrogen embrittlement, and it resists stress corrosion cracking in sulfide and chloride solutions. Alloy 751 is not recommended for use with ammonium hydroxide or strongly oxidizing acids.


Key Technology of Beryllium Copper(Heat treatment)

Age Hardening

Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.



Q1: Could you produce Beryllium Copper strip by Mill Hardened process.
A1: Yes, we could produce AM(TM00), 1/2HM(TM01).HM(TM04) XHM(TM06) XHMS(TM08).,we are the only factory could do harden strip in China.

Q2: What’s the advantages the Beryllium Copper of CUBERYLLIUM®.
A2: 1: The Biggest Coil weight could be reach 1200kg/Coil

2: We are the only one who melting by Vacuum semi-Continuous Furnace.

3: Surface further polishing for top clients.

Q3: Why you melting by Vacuum semi-Continuous Furnace.
A3: Could be get the Cast ingot without gas,smaller segregation, Grain Refinement

Q4:  What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.