Cube 2 Copper Alloy C17200 Strip 0.05x150mm Temper 3/4H HV200-220 Hot For Microswitch

Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xName | Cube2(C17200) Strip | Max Coil Wt. | 2T |
---|---|---|---|
Thinnest Thick. | 0.02mm | Max Width | 305mm |
Standard | ASTM B194, SAE J463, J461 | Hardness | 200~220HV |
Safe Handling | No Special Health Risk. | Machining Property | Good |
Surface | Bright/Polished | Flatness | Good |
State | 3/4H | Specification | 0.05x150mm |
Application | Microswitch Production | ||
High Light | cube 2 copper alloy C17200 Strip 0.05x150mm,C17200 Strip 0.05x150mm,copper alloy C17200 Strip Temper 3/4H 0.05x150mm |
Cube2(C17200) Strip 0.05x150mm Temper 3/4H (HV200~220) Hot For Microswitch Production
Product Normal Description:
Product Name: Cube2 strip
Grade: C17200
Standard: ASTM B194, SAE J463, J461
Product Specification: 0.05x150mm
State: H(TD04)
Typical Application: used for microswitch production
Product Brand: CUBERYLLIUM®
CUBERYLLIUM® manufactures copper beryllium in several distinct compositions.
These fall into two categories: high strength beryllium copper alloys 172(UNS. C17200),173(UNS. C17300),170(UNS. C17000), and copper alloys selected for high conductivity 751(UNS. 17510),750(UNS. 17500),741(UNS. 17410).
We also Supply Master alloy : CuBeryllium-200, CuBeryllium-275, CuBeryllium-350 and Cuberyllium-400 to global factory.
CUBERYLLIUM ®-172 also named Cube2--UNS. C17200 (CDA 172) Beryllium Copper is the most commonly utilized Copper Beryllium alloy and is notable for its highest strength and hardness compared to commercial copper alloys. C17200 alloy contains appr. 2% of beryllium and achieves its ultimate tensile strength can exceed 1360Mpa, while the hardness approaches Rockwell C45. Meanwhile, the electrical conductivity is a minimum of 22% IACS in the fully aged condition.C17200 also exhibits exceptional resistance to stress relaxation at elevated temperatures.
Chemical Composition of CuBe2/C17200 Copper Alloys (CUBERYLLIUM ®-172):
Product Grade: CUBERYLLIUM ®-172(UNS. C17200)
Beryllium(Be): 1.80-2.00%
Cobalt(Co) + Nickel(Ni): 0.20% Min
Cobalt(Co) + Nickel(Ni) + Iron(Fe): 0.60% Max
Lead: 0.02% Max
Copper(Cu): Balance
Note: Copper plus additions equal 99.5% Minimum.
Typical Physical Properties of CuBe2/C17200 Copper Alloys (CUBERYLLIUM ®-172):
Density (g/cm3): | 8.36 |
Density before age hardening (g/cm3): | 8.25 |
Elastic Modulus (kg/mm2 (103)): | 13.4 |
Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): | 17 x 10-6 |
Thermal Conductivity (cal/(cm-s-°C)): | 0.25 |
Melting Range (°C): | 870-980 |
Temper Designations of CuBe2/C17200 Copper Alloys (CUBERYLLIUM ®-172):
CuBeryllium Designation | ASTM | Mechanical and Electrical Properties of Copper Beryllium Strip | ||||||
Designation | Description | Tensile Strength (Mpa) |
Yield Strength 0.2% offset | Elongation Percent | HARDNESS (HV) |
HARDNESS Rockwell B or C Scale |
Electrical Conductivity (% IACS) |
|
A | TB00 | Solution Annealed | 410~530 | 190~380 | 35~60 | <130 | 45~78HRB | 15~19 |
1/2 H | TD02 | Half Hard | 580~690 | 510~660 | 12~30 | 180~220 | 88~96HRB | 15~19 |
H | TD04 | Hard | 680~830 | 620~800 | 2~18 | 220~240 | 96~102HRB | 15~19 |
HM | TM04 | Mill hardened |
930~1040 | 750~940 | 9~20 | 270~325 | 28~35HRC | 17~28 |
SHM | TM05 | 1030~1110 | 860~970 | 9~18 | 295~350 | 31~37HRC | 17~28 | |
XHM | TM06 | 1060~1210 | 930~1180 | 4~15 | 300~360 | 32~38HRC | 17~28 |
The Industrial Application Of CuBe2(C17200) Alloy:
Product Category | Product | Reason Category | Reason |
Industrial | Bourdon Tubes | Corrosion Resistance | Corrosion Resistance |
Bourdon Tubes | Forming Characteristics | Formability Good | |
Bourdon Tubes | Mechanical Properties | High Strength | |
Bourdon Tubes | Mechanical Properties | Low Elastic Modulus | |
Bushings | Corrosion Resistance | Corrosion Resistance | |
Bushings | Friction & Wear Properties | Galling Resistance | |
Bushings | Friction & Wear Properties | Wear Resistance | |
Bushings | Machining Characteristics | Machinability | |
Bushings | Mechanical Properties | High Strength |
Standard Tolerance of CuBe2 Strip C17200 (CUBERYLLIUM ®-172):
Tolerance Sheet | ||
(MM) | ||
Strip Thickness |
CuBeryllium® Standard Tolerance |
|
over | incl. | plus or minus |
0.03 | 0.08 | 0.003 |
0.08 | 0.1 | 0.004 |
0.1 | 0.15 | 0.005 |
0.15 | 0.2 | 0.006 |
0.2 | 0.25 | 0.007 |
0.25 | 0.4 | 0.008 |
0.4 | 0.55 | 0.009 |
0.55 | 0.7 | 0.01 |
0.7 | 0.9 | 0.015 |
0.9 | 1.5 | 0.025 |
Note: Tolerances apply to rolled and mill hardened strip. |
Product Photos:
FAQ:
Q1:Could you produce Beryllium Copper strip by Mill Hardened process.
A1:Yes, we could produce AM(TM00), 1/2HM(TM01).HM(TM04) XHM(TM06) XHMS(TM08).,we are the only factory could do harden strip in China.
Q2: What’s the advantages the Beryllium Copper of CUBERYLLIUM®.
A2: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous Furnace.
3:Surface further polishing for top clients.
Q3: Why you melting by Vacuum semi-Continuous Furnace.
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.