Welding Electrodes Beryllium Copper Alloy 10 Wire Tempered Round 0.8mm-1mm

Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Name | Beryllium Copper Alloy 10 Tempered Copper Round Wires | CUBERYLLIUM® Grade | CUBERYLLIUM® 750 |
---|---|---|---|
Diameter Range | 0.8mm-1mm | ASTM | ASTM B441 |
Temper | A(TB00), H(TD04), AT(TF00), HT(TH04) | Surface | Bright |
Package | On Spools And In Coils | Typical Application | For Welding Electrodes |
Shape For Available | Rod Or Coil Wire | Hot Working | Have Good Hot Working Property |
Cold Working | Have Excellent Cold Working Property | ||
High Light | beryllium copper welding wire 0.8mm,Welding Electrodes Beryllium Copper Alloy 10 wire,Alloy 10 becu copper |
Beryllium Copper Alloy 10 Tempered Copper Round Wires 0.8mm-1mm For Welding Electrodes
Product Description:
Name: Beryllium tempered copper round wires
Grade: Alloy 10
Specification: Thickness 0.8mm-1mm
Surface: Bright
State: A(TB00), H(TD04), AT(TF00), HT(TH04)
Features: Good strength and hardness
Application: For Welding Electrodes
CUBERYLLIUM® manufactures copper beryllium in several distinct compositions. These fall into two categories: alloys selected for high strength (Alloys 172,173,170) and alloys selected for high conductivity (Alloys 751,750,741). And Gost standard QBe2,QBe1.9Ti for Russia Market. Also Supply Master alloy : CuBeryllium-200; CuBeryllium-275);CuBeryllium-350 and Cuberyllium-400 to global factory.
Different Names and Specifications of Alloy 10 (C17500) Beryllium Copper:
Alloy | Specification |
Becu C175 C17500 CA 175 CDA 175 Alloy 10 Beryllium Copper Cobalt Beryllium Copper RWMA Class 3 |
ASTM B441 ASTM B534 ASTM B888 ASTM B937 ASTM B938 MIL - C - 81021 |
Chemical Composition of Beryllium Copper Alloy 10:
CUBERYLLIUM® Brand | UNS-Number | Beryllium | Cobalt | Fe | Si | Copper |
Cuberyllium-C750 | C17500 | 0.40-0.70 | 2.4~2.7 | <0.1 | <0.2 | Balance |
Note: Copper plus additions equal 99.5% Min.
Typical Physical Properties of Beryllium Copper Alloy 10:
Density | 8.83 | g/cm3 |
Density before age hardening | 8.75 | g/cm3 |
Melting Range | 1000~1070 | ℃ |
Elastic Modulus | 14.1 | (kg/mm2 (103) |
Thermal Expansion Coefficient | 18 x 10 -6 | 20 °C to 200 °C m/m/°C |
Thermal Conductivity | 0.48 | cal/(cm-s-°C) |
Mechanical and Electrical Properties of Beryllium Copper Alloy 10 Round Wires:
Temper(*) | Heat Treatment |
Tensile Strength Mpa |
Elongation Percent (Min) |
Electrical Conductivity Percent IACS |
---|---|---|---|---|
A(TB00) | / | 240~380 | 20~60 | 20~30 |
H(TD04) | / | 440~550 | 2~20 | 20~30 |
AT(TF00) | 3 hr 490℃ | 690~900 | >10 | 45~60 |
HT(TH04 | 2 hr 490 ℃ | 750~960 | >10 | 48~60 |
Related Material Specifications of Beryllium Copper Alloy 10:
Wires: ASTM B441
Rods/Bars/Tubes: ASTM B441, SAE J461, 463; RWMA Class 3
Strips: ASTM B534
Sheets: ASTM B534
Plates: ASTM B534, SAE J461, RWMA Class 3
European Standards: CuCo2Be, CuCoBe, UNS. C17500, Alloy 10, DIN 2.1285, CW104C to EN
Note:
ASTM: American Society for Testing and Materials
SAE: Society of Automotive Engineers
AMS: Aerospace Materials Specification(Published by SEA)
RWMA: Resistance Welder Manufacturers' Association
Note: Unless otherwise specified, material will be produced by ASTM.
Typical Applications of Beryllium Copper Alloy 10:
• Bearings and bushes |
• Plastic moulds |
• Corrosion resistant components |
• Current carrying springs |
• Welding electrodes |
• Electrical and electronic connectors |
Product Photo:
Weldability
Soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding are all recommended
Hot & Cold Workability
Good hot working properties. Excellent cold working properties.
Key Technology of Beryllium Copper(Heat treatment)
Age Hardening
Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.
FAQ:
Q1:Could you produce Beryllium Copper strip by Mill Hardened process.
A1:Yes, we could produce AM(TM00), 1/2HM(TM01).HM(TM04) XHM(TM06) XHMS(TM08).,we are the only factory could do harden strip in China.
Q2: What’s the advantages the Beryllium Copper of CUBERYLLIUM®.
A2: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous Furnace.
3:Surface further polishing for top clients.
Q3: Why you melting by Vacuum semi-Continuous Furnace.
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.