ASTM C17510 Beryllium Copper Sheet Bar Thermal Conductivity High

Place of Origin China
Brand Name CUBERYLLIUM®
Certification ISO ROHS
Model Number ASTM C17510
Minimum Order Quantity 30kg
Price USD 30~50/KG
Packaging Details Pack in coil+waterproofing winding film+Drier+Wooden Case
Delivery Time 10~15 Working days
Payment Terms L/C, T/T
Supply Ability 50T/Month

Contact me for free samples and coupons.

Whatsapp:0086 18588475571

Wechat: 0086 18588475571

Skype: sales10@aixton.com

If you have any concern, we provide 24-hour online help.

x
Product Details
Name ASTM C17510 Beryllium Copper Round Bar ASTM ASTM B441
Surface Bright, Polish Specification All Sizes
State A(TB00),H(TD04),AT(TF00),HT(TH04) Typical Application Electrical And Industrial
Shape For Available Rod&Bar Brand CUBERYLLIUM®
Density 8.83g/cm3 Length Clients' Requirement
Diameter 8-30mm
High Light

ASTM c17510 beryllium copper sheet

,

alloy c17510

,

c17510 thermal conductivity high

Leave a Message
Product Description

ASTM C17510 Beryllium Copper Round Bar With Highly Thermal And Electrical Conductivity

Product Description:

Name: Beryllium copper round bar

Grade: ASTM C17510

End Product Form: Rods/ Bars

Standard: ASTM B441, SAE J461,

State of product: A(TB00),H(TD04),AT(TF00),HT(TH04)

Processing: Seamless / Welding

Feature: With high strength and high conductivity

Package: Pack in coil+waterproofing winding film+Drier+Wooden Case

Specification: 1, Length: according customers' requirement

                       2, Diameter: 8-30mm

 

CUBERYLLIUM® manufactures copper beryllium in several distinct compositions. These fall into two categories: alloys selected for high strength (Alloys 172,173,170) and alloys selected for high conductivity (Alloys 751,750,741). And Gost standard QBe2,QBe1.9Ti for Russia Market. Also Supply Master alloy : CuBeryllium-200; CuBeryllium-275);CuBeryllium-350 and Cuberyllium-400 to global factory.

 

Beryllium copper has its reasonable share of common names. You will listen referred to as BeCu, Copper Beryllium, Beryllium Bronze, and Spring Copper. Anytime you hear those terms, they're in reference to Beryllium Copper. Beryllium round bars are accessible as high strength and high conductivity alloys. 

 

CUBERYLLIUM ®-751 also named -C17510 (CDA 1751) combine moderate yield strength, up to 960Mpa(140ksi), with electrical and thermal conductivity from 45 to 60 % of pure copper. Alloys 750 and 751 are available in wrought product forms and can be supplied fully hardened. Hardened products are identified by the temper designation AT or HT, and have good formability.

 

Chemical Composition of ASTM C17510 Beryllium Copper Alloys:

CUBERYLLIUM® Brand UNS-Number Beryllium Nickel Cobalt+Nickel Cobalt+Nickel+Iron Lead Copper
Cuberyllium-C751 C17510 0.20 ~ 0.60% 1.40 ~ 2.20% - - - Balance

 

Related material specifications of ASTM C17510 Beryllium Copper Alloys:

Rods/Bars/Tubes: ASTM B441, SAE J461, 463; RWMA Class 3

European Standards: CuNi2Be, CuNiBe, Alloy 3, DIN.2.0850, CW110C to EN

 

Note: 

ASTM: American Society for Testing and Materials

SAE: Society of Automotive Engineers

AMS: Aerospace Materials Specification(Published by SEA)

RWMA: Resistance Welder Manufacturers' Association

Note: Unless otherwise specified, material will be produced by ASTM.


Typical Physical Properties of ASTM C17510 Beryllium Copper Alloys:

Density 8.83 g/cm3
Density before age hardening 8.75 g/cm3
Melting Range 1000~1070
Elastic Modulus 14.10 (kg/mm2 (103)
Thermal Expansion Coefficient 18 x 10 -6 20 °C to 200 °C m/m/°C
Thermal Conductivity 0.57 cal/(cm-s-°C)

 

Typical Applications for ASTM C17510 Beryllium Copper Alloys:

A: Electrical: Instrument Parts, Connectors, Heavy Duty, Relay Parts, Conductors, Switch Parts, Fuse Clips;

B: Fasteners: Washers, Fasteners, Lock Washers, Retaining Rings, Roll Pins, Screws, Bolts;

C: Industrial: High Flux Electromagnets, Thermal Transfer Plates, Welding Equipment, Springs, Die Casting Plunger Tips.

 

Mechanical Properties of C17510 Beryllium Copper Alloy:

Properties Metric Imperial
Hardness, Rockwell B (any thickness) ≥ 90.0 ≥ 90.0
Tensile strength at break (@thickness ≥50.8 mm/ @thickness ≥2.00 in) ≥ 607 MPa ≥ 88000 psi
Tensile strength at break 9@thickness 25.4-50.8 mm/ @thickness 1.00 - 2.00 in) ≥ 621 MPa ≥ 90000 psi
Tensile strength at break (@thickness 25.4 mm/ @thickness ≤1.00 in) ≥ 648 MPa ≥ 94000 psi
Tensile strength, yield (@strain 0.500%, thickness 50.8 mm/ @strain 0.500 %, thickness 2.00 in) ≥ 607 MPa ≥ 88000 psi
Tensile strength, yield (@strain 0.500%, thickness 25.4-50.8 mm/ @strain 0.500%, thickness 1.00 - 2.00 in) ≥ 621 MPa ≥ 90000 psi
Tensile strength, yield (@strain 0.500%, thickness 25.4 mm/ @strain 0.500%, thickness 1.00 in) ≥ 648 MPa ≥ 94000 psi
Modulus of elasticity 131 GPa 19000 ksi
Poissons ratio 0.267 0.267
Shear modulus 51.7 GPa 7500 ksi

 

 

Product Photo:

ASTM C17510 Beryllium Copper Sheet Bar Thermal Conductivity High 0

 

 

Weldability

Soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding are all recommended

 

Hot & Cold Workability

Good hot working properties. Excellent cold working properties.

 

Key Technology of Beryllium Copper(Heat treatment)

Age Hardening

Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.

 

FAQ:

Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?

A1: 1: The Biggest Coil weight could be reach 1200kg/Coil

2:We are the only one who melting by Vacuum semi-Continuous Furnace.

3:Surface further polishing for top clients.

Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid before the delivery.

Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement

Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.