CuCo2Be Cobalt C17500 Beryllium Copper Strip Hardness 200-280HV

CuCo2Be UNS.C17500 Cobalt Beryllium Copper Strip Utilized In The Industry Applications

Product Description:

Name: Cobalt Beryllium Copper Strip

Grade: CuCo2Be, UNS.C17500

End Product Form: Strips, Sheet, Coils

Standard: ASTM B534

Specification: According customers' requirement

CUBERYLLIUM® manufactures copper beryllium in several distinct compositions. These fall into two categories: alloys selected for high strength (Alloys 172,173,170) and alloys selected for high conductivity (Alloys 751,750,741). And Gost standard QBe2,QBe1.9Ti for Russia Market. Also Supply Master alloy : CuBeryllium-200; CuBeryllium-275);CuBeryllium-350 and Cuberyllium-400 to global factory.

C17500 Chemical Composition:

Executive standard:ASTM/GB/T5233-2001/EN12163(%max., unless shown as range or min.)

Related material specifications

Strips: ASTM B534

Sheets: ASTM B534

European Standards: CuCo2Be, CuCoBe, UNS. C17500, Alloy 10, DIN 2.1285, CW104C to EN

Note: 

ASTM: American Society for Testing and Materials

SAE: Society of Automotive Engineers

AMS: Aerospace Materials Specification(Published by SEA)

RWMA: Resistance Welder Manufacturers' Association

Note: Unless otherwise specified, material will be produced by ASTM.

Typical Physical Properties:

Typical Applications for CuCo2Be/C17500 Cobalt Beryllium Copper Alloys:

A: Electrical Industry: Switch Parts, Connectors, Spring Connectors, Fuse Clips, Relay Parts;

B: Fasteners: Washers, Fasteners;

C: Industrial: Spring, Resistance Welding Equipment, Resistance and Spot Welding Tips, Seam Welding Dies, Die-Casting Plunger Tips, Tooling for Plastic Moulds.

Product Photo:

Weldability

Soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding are all recommended

Hot & Cold Workability

Good hot working properties. Excellent cold working properties.

Key Technology of Beryllium Copper(Heat treatment)

Age Hardening

Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.

FAQ:

Q1:Could you produce Beryllium Copper strip by Mill Hardened process.
A1:Yes, we could produce AM(TM00), 1/2HM(TM01).HM(TM04) XHM(TM06) XHMS(TM08).,we are the only factory could do harden strip in China.

Q2: What’s the advantages the Beryllium Copper of CUBERYLLIUM®.
A2: 1: The Biggest Coil weight could be reach 1200kg/Coil

2:We are the only one who melting by Vacuum semi-Continuous Furnace.

3:Surface further polishing for top clients.

Q3: Why you melting by Vacuum semi-Continuous Furnace.
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement

Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.