CuCo2Be C17500 Beryllium Copper Rod Outer Diameter 0.06-2.00mm

  • CuCo2Be C17500 Beryllium Copper Rod Outer Diameter 0.06-2.00mm
  • CuCo2Be C17500 Beryllium Copper Rod Outer Diameter 0.06-2.00mm
Place of Origin China
Brand Name CUBERYLLIUM
Certification ISO ROHS
Model Number CuCo2Be
Minimum Order Quantity 30kg
Price USD 30～50/KG
Packaging Details Pack in coil+waterproofing winding film+Drier+Wooden Case
Delivery Time 10～15 Working days
Payment Terms L/C, T/T
Supply Ability 50T/Month

Contact me for free samples and coupons.

Whatsapp:0086 18588475571

Wechat: 0086 18588475571

Skype: sales10@aixton.com

If you have any concern, we provide 24-hour online help.

x
Product Details
Name Cobalt Beryllium Copper Rod ASTM ASTM B441
Surface Bright Outer Diameter 0.06 ~ 2.00mm
State AT(TF00) Heat Treatment 3 Hr 480℃
Typical Application Electrical Industry Shape For Available Rod&Bar
Hardness B92~100 Rockwell B Scale Brand CUBERYLLIUM®
Tensile Strength 680~900 Mpa Elongation Percent 10~30 Min
Electrical Conductivity 45~60% IACS
High Light

CuCo2Be C17500 Beryllium Copper Rod 0.06-2.00mm

,

Beryllium Copper Rod 0.06-2.00mm

,

C17500 beryllium oxide alloy
Leave a Message
Product Description

CuCo2Be Cobalt Beryllium Copper Rod Out Diameter 0.06-2.00mm For Electrical Industry

 

CUBERYLLIUM® manufactures copper beryllium in several distinct compositions. These fall into two categories: alloys selected for high strength (Alloys 172,173,170) and alloys selected for high conductivity (Alloys 751,750,741). And Gost standard QBe2,QBe1.9Ti for Russia Market. Also Supply Master alloy : CuBeryllium-200; CuBeryllium-275);CuBeryllium-350 and Cuberyllium-400 to global factory.

 

C17500 Beryllium Copper Rod Specification

Name C17500 Beryllium Copper Rod, CuCo2Be Cobalt Copepr Rod, Alloy 10 Copper Rod
Standard of Rod ASTM B441, SAE J461, 463; RWMA Class 3
Different Shape We offer C17500 Rods/Bars in various shapes, sizes, strandards and grades to offer wide customization options to our customers.
Processing Seamless / Welding
Application

A: Electrical Industry: Switch Parts, Connectors, Spring Connectors, Fuse Clips, Relay Parts;

B: Fasteners: Washers, Fasteners;

C: Industrial: Spring, Resistance Welding Equipment, Resistance and Spot Welding Tips, Seam Welding Dies, Die-Casting Plunger Tips, Tooling for Plastic Moulds.

 

 

Chemical Composition of CuCo2Be Cobalt Beryllium Copper Alloy:

CUBERYLLIUM® Brand UNS-Number Beryllium Cobalt Nickel Cobalt+Nickel Lead Copper
Cuberyllium-C750 C17500 0.40-0.70 2.4～2.7 - - - Balance

 


Typical Physical Properties of CuCo2Be Cobalt Beryllium Copper Alloy:

Density 8.83 g/cm3
Density before age hardening 8.75 g/cm3
Melting Range 1000~1070 ℃
Elastic Modulus 14.1 (kg/mm2 (103)
Thermal Expansion Coefficient 18 x 10 -6 20 °C to 200 °C m/m/°C
Thermal Conductivity 0.48 cal/(cm-s-°C)

 

 

Mechanical and Electrical Properties of Copper Beryllium Rod&Bar and Tube of CUBERYLLIUM®-750:

Temper(*) Diameter Heat Treatment

Tensile Strength

Mpa

Elongation Percent

(Min)

Electrical Conductivity

Percent IACS

Hardness Rockwell

B Scale
A(TB00) ALL SIZE / 240~380 20~40 20~35 B20~50

H(TD04)

 ALL SIZE / 440~550 10~20 20~35 B20~30
AT(TF00) ALL SIZE 3 hr 480℃ 680~900 10~30 45~60 B92~100
HT(TH04 ALL SIZE 2 hr 480 ℃ 750~960 5~30 48~60 B95~102

 

 

Product Photo:

CuCo2Be C17500 Beryllium Copper Rod Outer Diameter 0.06-2.00mm 0

 

 

Weldability

Soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding are all recommended

 

Hot & Cold Workability

Good hot working properties. Excellent cold working properties.

 

Key Technology of Beryllium Copper(Heat treatment)

Age Hardening

Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.

 

FAQ:

Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?

A1: 1: The Biggest Coil weight could be reach 1200kg/Coil

2:We are the only one who melting by Vacuum semi-Continuous Furnace.

3:Surface further polishing for top clients.

Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid before the delivery.

Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement

Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.

Tags:

c17500 copper

Beryllium Copper Strips 0.3x30mm

UNS c17500 copper Beryllium Alloys